KEKERASAN PERMUKAAN RESIN KOMPOSIT HYBRID SETELAH DIRENDAM DALAM MINUMAN ENERGI pH ASAM

ADITYA HAYU NASTITI, 020610151 (2012) KEKERASAN PERMUKAAN RESIN KOMPOSIT HYBRID SETELAH DIRENDAM DALAM MINUMAN ENERGI pH ASAM. Skripsi thesis, UNIVERSITAS AIRLANGGA.

[img]
Preview
Text (ABSTRAK)
gdlhub-gdl-s1-2012-nastitiadi-23116-kg-09-12-t.pdf

Download (361kB) | Preview
[img] Text (FULLTEXT)
gdlhub-gdl-s1-2012-nastitiadi-19392-kg0912-k.pdf
Restricted to Registered users only

Download (1MB) | Request a copy
Official URL: http://lib.unair.ac.id

Abstract

Hybrid composite resin has a high mechanical strength and it has a less shrinkage during polimerisation. Composite resin may able to absorb liquid, chemical substance, and acid solution surround it. Purpose. To observe the difference of hybrid composite resin surface hardness after being immersed in acid energy drink pH 3,2; 3,7; 3,9 for 2 hours. Method. 28 specimens were made using a 5 mm in diameter and 2 mm in thickness mold. The hybrid composite resin were polymerized for 40 seconds with Light Emitting Diode and divided into 3 experimental groups and 1 control group. The experimental groups were immersed in different energy drink (pH 3,2; 3,7; 3,9) for each group and the control group was immersed in aquadest for 2 hours. The surface hardness was measured from three sites of specimens’ surface with micro Vickers hardness tester. Data were analyzed using One Way ANOVA test. Results. This showed there was significant differences in surface hardness between sample groups (α < 0,05). Conclusion. The surface hardness of hybrid composite resin were decreased after being immersed in acid energy drinks (pH 3,2; 3,7; 3,9) for 2 hours.

Item Type: Thesis (Skripsi)
Additional Information: KKA KK KG 09/12 Nas k
Uncontrolled Keywords: HYBRID COMPOSITE
Subjects: R Medicine
R Medicine > RK Dentistry > RK1-715 Dentistry
Divisions: 02. Fakultas Kedokteran Gigi
Creators:
CreatorsEmail
ADITYA HAYU NASTITI, 020610151UNSPECIFIED
Contributors:
ContributionNameEmail
ContributorAnita Yuliati, Prof. Dr. , drg., M.Kes.UNSPECIFIED
Depositing User: Dwi Prihastuti
Date Deposited: 29 Feb 2012 12:00
Last Modified: 02 Aug 2016 08:00
URI: http://repository.unair.ac.id/id/eprint/19358
Sosial Share:

Actions (login required)

View Item View Item