Indra Mulyawan, - and Coen Pramono Danudiningrat, - and Pratiwi Soesilawati, - and Aulanni’am, - and Anita Yuliati, - and Heri Suroto, - and Taufan Bramantoro, - and Andra Rizqiawan, - and Seong-Yong Moon, - (2022) The Characteristic of Demineralized Dentin Material Sponge as Guide Bone Regeneration Based on the FTIR and SEM-EDX Tests. European Journal of Dentistry, 2 (2). ISSN 13057464, 13057456

	Text (NASKAH) The Characteristics of Demineralized Dentin.pdf Download (4MB)
	Text (TURNITIN) 20.The Characteristics of Demineralized Dentin Material Sponge as Guided Bone Regeneration Based on the FTIR and SEM-EDX Tests.pdf Download (2MB)
	Text (VALIDASI) 20.Dr.Pratiwi ( The Caracteristic of Demineralized..).pdf Download (1MB)

Abstract

Objective The objective of this study was to determine the characteristics of demineralized dentin material sponge (DDMS). Material and Methods An observational study was conducted on DDMS and BPCM. Fourier transform infrared (FTIR) test was performed to determine the characterizations of the materials. Scanning electron microscope-electron dispersive X-ray spectroscopy (SEM-EDX) test was performed to observe the elements contained in the materials. Results The infrared spectrum of the DDMS and BPCM functional groups showed the same pattern in each variation, and no significant differences were found. According to SEM analysis, the cavities that make up the membrane were spotted on the surface. Besides, according to the SEM-EDX analysis, DDMS contained chlorine, carbon, and calcium, while BPCM contained carbon, oxygen, and sulfur. Conclusion DDMS has the potential to be a biomaterial for bone tissue engineering in terms of the characteristics. DDMS had a structure that almost resembles BPCM as seen from the results of the FTIR graph between DDMS and BPCM. The morphological structure of the two materials in the SEM test appeared to have porosity with various sizes.

Actions (login required)

View Item