CINITRA ANINDYA, 020911124 (2013) KOROSI NIKEL PADA STAINLESS STEEL CROWN DALAM SALIVA ARTIFISIAL. Skripsi thesis, UNIVERSITAS AIRLANGGA.

Preview	Text (ABSTRAK) gdlhub-gdl-s1-2013-anindyacin-23344-5.ABSTRAK.pdf Download (179kB) | Preview
	Text (FULLTEXT) gdlhub-gdl-s1-2013-anindyacin-23344-1.FULLTEXT.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

Stainless steel crown (SSC) which contained nickel chromium (NiCr) alloys are often used for restoration in the field of pediatric dentistry that requiring strength, such as crown. NiCr alloys containing 68-80% nickel, 11.9 to 26.3% chromium, and additional components such as molybdenum, niobium, beryllium, silicon, aluminum, and titanium. Unfavorable effects of dental metals is due to the corrosion process, which resulted in the release of metal ions. In the oral cavity, corrosion process occurs due to the reaction of metal with oral electrolyte fluid which called saliva. Nickel was choosen to be measured because nickel is the main composition of SSC. Purpose: To determine the number of nickel corroded in artificial saliva with two diferrent pH which are neutral pH (7) and acidic pH (5) on immersing for 1, 3, and 7 days. Methods: A whole research sample divided into three groups. Each group consists of eight samples. Group 1 as a control group were using an aquadest as a media, group 2 were using artificial saliva with acidic pH (5), group 3 were using artificial saliva with neutral pH (7). All of the samples immersed for 1, 3, and 7 days. Then, the level of nickel corroded measured with Atomic absorption spectrophotometer (AAS). Results: The level of nickel corroded increased from day 1 to 3, and the peak is on the 7th day, and the level of nickel corroded that immersed in acidic artificial saliva were higher than the group that immersed in neutral artificial saliva. Conclusion: The highest level of nickel corroded found at the group that immersed in acidic artificial saliva and on the day 7 of immersion.

Item Type:	Thesis (Skripsi)
Additional Information:	KKA KK KG.58/13 Ani k
Uncontrolled Keywords:	STAINLESS STEEL CROWN
Subjects:	R Medicine > RK Dentistry > RK1-715 Dentistry
Divisions:	02. Fakultas Kedokteran Gigi
Creators:	Creators NIM CINITRA ANINDYA, 020911124 UNSPECIFIED
Contributors:	Contribution Name NIDN / NIDK Thesis advisor Prawati Nuraini, drg.,M.Kes.,Sp.KGA(K) UNSPECIFIED Thesis advisor Tania Saskianti, drg.,Sp.KGA.,Ph.D. UNSPECIFIED
Depositing User:	Mrs Nadia Tsaurah
Date Deposited:	13 Mar 2013 12:00
Last Modified:	22 Jul 2016 03:19
URI:	http://repository.unair.ac.id/id/eprint/19047
Sosial Share:

Actions (login required)

View Item