Fauziah Diajeng Retnaningsih (2020) Pengaruh pH Kombinasi Kalsium Hidroksida–Propolis- Propylene Glycol Terhadap Modulus Elastisitas Dentin. Other thesis, UNIVERSITAS AIRLANGGA.
![[img]](https://repository.unair.ac.id/style/images/fileicons/text.png) |
Text
1. HALAMAN JUDUL.pdf Download (503kB) |
|
Text
2. ABSTRACT.pdf Download (94kB) |
|
Text
3. DAFTAR ISI.pdf Download (154kB) |
|
Text
4. BAB I PENDAHULUAN.pdf Download (145kB) |
|
Text
5. BAB 2 TINJAUAN PUSTAKA.pdf Restricted to Registered users only until 14 August 2023. Download (323kB) |
|
Text
6. BAB 3 KERANGKA KONSEP.pdf Restricted to Registered users only until 14 August 2023. Download (229kB) |
|
Text
7. BAB 4 METODE PENELITIAN.pdf Restricted to Registered users only until 14 August 2023. Download (288kB) |
|
Text
8. BAB 5 HASIL PENELITIAN.pdf Restricted to Registered users only until 14 August 2023. Download (146kB) |
|
Text
9. BAB 6 PEMBAHASAN.pdf Restricted to Registered users only until 14 August 2023. Download (109kB) |
|
Text
10. BAB 7 KESIMPULAN DAN SARAN.pdf Restricted to Registered users only until 14 August 2023. Download (90kB) |
|
Text
11. DAFTAR PUSTAKA.pdf Download (158kB) |
|
Text
12. LAMPIRAN.pdf Restricted to Registered users only until 14 August 2023. Download (776kB) |
Abstract
Background: Calcium hydroxide is a pulp capping material that is often used in dentistry but has many lacks. Propolis is a resin compound derived from honey bee wax (Apis mellifera), derived from saliva and several enzymes, which bees use to build their hives. Propylene glycol (PG) is a clear, colorless, odorless liquid with a slight characteristic resembling glycerin and is often used as a vehicle in endodontic fields.Objective : To determine the effect of pH on elastic modulus of dentin which exposed to calcium hydroxide, calcium hydroxide + propolis, and calcium hydroxide + propolis + propylene glycol. Materials and Methods: Samples were divided into 2 groups, the pH group and the elastic modulus of dentin group. The pH group was divided into 3 groups, with each consisting of 9 samples; group 1: calcium hydroxide + aquadest, group 2: calcium hydroxide + propolis, group 3: calcium hydroxide + propolis + propylene glycol. The modulus elasticity group is divided into 4 groups: group 1: calcium hydroxide + aquades, group 2: calcium hydroxide + propolis, group 3: calcium hydroxide + propolis + propylene glycol, group 4: dentin. After 7 days, the pH sample was measured with a pH meter, and the elastic modulus sample was measured by a universal testing machine. The measurement results are normality test, homogeneity test and statistical test with one way ANOVA, comparative test with Tukey HSD and correlation test with Pearson. Results: One way ANOVA analysis data showed significant differences between groups (p <0.05) and the correlation test showed a relationship between pH and elastic modulus of dentin. Conclusions: There is a correlation between the pH value with the elastic modulus of dentin where the higher the pH value (alkaline environment), the higher of the elastic modulus of dentin is exposed (the more rigid).
| Item Type: | Thesis (Other) | ||||||
|---|---|---|---|---|---|---|---|
| Additional Information: | KKA KK PPDGS Kon 25-20 Ret p | ||||||
| Uncontrolled Keywords: | Calcium hydroxide, propolis, propylene glycol, pH, modulus elastisitas dentin | ||||||
| Subjects: | R Medicine > RK Dentistry > RK641-667 Prosthetic dentistry. Prosthodontics | ||||||
| Divisions: | 02. Fakultas Kedokteran Gigi > Concervative | ||||||
| Creators: |
|
||||||
| Contributors: |
|
||||||
| Depositing User: | Andri Yanti | ||||||
| Date Deposited: | 14 Aug 2020 04:55 | ||||||
| Last Modified: | 14 Aug 2020 04:55 | ||||||
| URI: | http://repository.unair.ac.id/id/eprint/97358 | ||||||
| Sosial Share: | |||||||
Actions (login required)
 |
View Item |