Piscensa Lathiefa Ramadhani (2015) Sintesis, Karakterisasi, Dan Aplikasi Lapis Tipis Tio2-Sio2 Termodifikasi Surfaktan Pada Kaca Sebagai Material Self Cleaning. Skripsi thesis, UNIVERSITAS AIRLANGGA.

	Text 1. HALAMAN JUDUL .pdf Download (424kB)
	Text 2. ABSTRAK.pdf Download (294kB)
	Text 3. DAFTAR ISI.pdf Download (344kB)
	Text 4. BAB I PENDAHULUAN.pdf Download (332kB)
	Text 5. BAB II TINJAUAN PUSTAKA.pdf Restricted to Registered users only until 1 April 2023. Download (546kB) | Request a copy
	Text 6. BAB III METODE PENELITIAN.pdf Restricted to Registered users only until 1 April 2023. Download (326kB) | Request a copy
	Text 7. BAB IV HASIL DAN PEMBAHASAN.pdf Restricted to Registered users only until 1 April 2023. Download (702kB) | Request a copy
	Text 8. BAB V KESIMPULAN DAN SARAN.pdf Restricted to Registered users only until 1 April 2023. Download (291kB) | Request a copy
	Text 9. DAFTAR PUSTAKA.pdf Download (337kB)
	Text 10. MPIRAN.pdf Restricted to Registered users only until 1 April 2023. Download (1MB) | Request a copy

Abstract

Telah dilakukan pelapisan material self cleaning TiO2-SiO2 termodifikasi surfaktan. TiO2-SiO2 dibuat melalui sintesis dengan titanium tetraisopropoksida, sol SiO2, dan surfaktan etilen glikol. Karakterisasi hasil TiO2-SiO2 dilakukan dengan XRD, FTIR, SEM-EDX, dan sudut kontak. Karakterisasi menggunakan XRD menunjukkan bahwa TiO2 yang telah disintesis adalah TiO2 anatase. Karakterisasi menggunakan Spektroskopi Inframerah menunjukkan bahwa pada bilangan gelombang 910 cm-1 dan 925 cm-1 terdapat ikatan Ti-O-Si. Karakterisasi pada SEM-EDX menunjukkan bahwa SiO2 dapat memperbesar pori permukaan kaca yang telah dilapisi dengan TiO2-SiO2, dan uji sudut kontak menunjukkan bahwa lapis tipis TiO2-SiO2 komposit 30:70, 50:50, dan 70:30 mempunyai sifat hidrofilik. Komposit TiO2-SiO2 yang memberikan % degradasi congo red terbesar adalah 50:50 selama tiga jam yaitu sebesar 77,24%.